Vol.9, No 1, 2011 pp. 1 - 9
UDC 620.178.3:691.32+677.52=111
DOI: 10.2298/FUACE1101001K


EFFECT OF SIZE AND SHAPE OF SPECIMEN ON COMPRESSIVE STRENGTH OF GLASS FIBER REINFORCED CONCRETE (GFRC)
M.V. Krishna Rao, P. Rathish Kumar, B. Srinivas
Department of Civil Engineering CBIT, Hyderabad and NIT Warangal
E-mail: drrateesh@gmail.com
Concrete is a versatile material with tremendous applications in civil engineering construction. Structural concrete elements are generally made with concrete having a compressive strength of 20 to 35 MPa. Lately, there is an increase in use of high strength concrete (HSC) in major construction projects such as high-rise buildings, and bridges involving members of different sizes and shapes. The compressive strength of concrete is used as the most basic and important material property in the design of reinforced concrete structures. It has become a problem to use this value as the control specimen sizes and shapes are different from country to country. In India, the characteristic compressive strength is usually measured based on 150 mm cubes [1]. But, the ACI code of practice specifies the design compressive strength based on the standard 150  300 mm cylinders [2]. The use of 100  200 mm cylinders gained more acceptance as the need to test high strength concrete increases [3]. In this context the size and shape of concrete becomes an important parameter for the compressive strength. In view of the significance of compressive strength of concrete and due to the fact that the structural elements of different sizes and shapes are used, it is proposed to investigate the effect of size and shape of the specimen on the compressive strength of concrete. In this work, specimens of plain as well as Glass Fiber Reinforced Concrete (GFRC) specimens are cast in order to carry out a comparative study.
Key words: compressive strength, size effect, glass fiber reinforced concrete.

UTICAJ VELIČINE I OBLIKA PROBNOG TELA NA ČVRSTOĆU PRI PRITISKU BETONA ARMIRANIH STAKLENIM VLAKNIMA (GFRC)
Beton je materijal sa raznovrsnom primenom u građevinarstvu. Betonski konstruktivni elementi su naješće napravljeni od betona koji imaju visoku čvrstoću na pritisak od 20 do 35 MPa. U poslednje vreme povećana je upotreba betona visoke čvrstoće na pritisak (HSC) u okviru velikih građevinskih projekata, kao što su oblakoderi i mostovi koji imaju elemente različitih oblika i veličina. Čvrstoća pri pritisku betona je korišćena kao najosnovnija i najvažnija osobina materijala kod projektovanja objekata od armiranog betona. Korišćenje ovih parametara postaje problem, jer se oblik i veličina probnih tela razlikuju od zemlje do zemlje. U Indiji se karakteristična čvrstoća pri pritisku meri na kockama koje imaju ivicu od 150 mm [1]. Međutim, pravilnik ACI predviđa projektovanje na temelju čvrstoća na pritisak dobijenih na standardnim cilindrima dimenzija 150  300 mm [2]. Korišćenje cilindara dimenzija 100  200 mm postaje sve više prihvaćeno, kako raste potreba za ispitivanjem betona visoke čvrstoće [3]. U ovom smislu, veličina i oblik betonskog tela postaje važan parametar kod čvrstoće na pritisak. U svetlu važnosti čvrstoće na pritisak betona i zahvaljujući činjenici da se koriste konstruktivni elementi različitih veličina i oblika, predlaže se ispitivanje uticaja veličine i oblika probnih tela na rezultate čvrstoće betona na pritisak. U ovom radu su pripremljena probna tela od običnog i betona ojačanog staklenim vlaknima (GFRC), da bi se izvršila uporedna analiza.
Ključne reči: čvrstoća pri pritisku, efekat veličine, beton armiran staklenim vlaknima